View article: Investigation on the Mechanism of Hot Deformation Behavior of Aluminum Single Crystals Based on Grain Orientation
Investigation on the Mechanism of Hot Deformation Behavior of Aluminum Single Crystals Based on Grain Orientation Open
Aluminum alloys are widely used in transportation industries due to their excellent specific strength, stiffness, and formability. Modifying the texture of aluminum alloys can further enhance their mechanical properties. This study explore…
View article: The effects of cyclic-strengthening interrupted aging on the microstructure evolution and stress corrosion resistance of aluminum alloy
The effects of cyclic-strengthening interrupted aging on the microstructure evolution and stress corrosion resistance of aluminum alloy Open
The stress corrosion is likely to occur in high-strength aluminium alloys especially in corrosive environments, which is a key factor affecting the service safety of aluminium alloy components. In this study, a new kind of aging method, in…
View article: Effect of Corrosion Environment on Mechanical Behavior of 5083/6005A Welded Joints
Effect of Corrosion Environment on Mechanical Behavior of 5083/6005A Welded Joints Open
The corrosion fatigue behavior of welded joints is a critical concern in the transportation industry, which shortens their service life. In this paper, the corrosion damage of 5083/6005A welded joints exposed to different conditions (3.5% …
View article: Influence of Mg Content on the Corrosion Behavior and Precipitation of Aged Al-Cu-Li-xMg Alloys
Influence of Mg Content on the Corrosion Behavior and Precipitation of Aged Al-Cu-Li-xMg Alloys Open
Aluminum (Al)–copper (Cu)–lithium (Li) alloys are susceptible to environmental degradation, which limits the in-service lifetime of the components. Because of their complex composition, there are seldom studies focusing on corrosion behavi…
View article: Effects of microstructure on tensile properties of AA2050-T84 Al-Li alloy
Effects of microstructure on tensile properties of AA2050-T84 Al-Li alloy Open
The effect of microstructure evolution on the tensile properties of 2050 Al−Li alloy thick plate aged at 150 °C with 80 mm in thickness (t) was studied from a microstructural perspective. Scanning electron microscope, optical microscope, t…