View article: The Interaction Between Oxidation-Related Phenomena Along Grain Boundaries on Surface Crack Formation in Continuous Casting
The Interaction Between Oxidation-Related Phenomena Along Grain Boundaries on Surface Crack Formation in Continuous Casting Open
Oxidation-related surface defect formation in continuous casting is an under-researched topic, as most of the experiments, which aim to define surface defect mechanisms, are performed under a protective atmosphere. However, intergranular o…
View article: Investigation on the Susceptibility to Surface Crack Formation in Continuous Casting by a New In Situ Bending Test
Investigation on the Susceptibility to Surface Crack Formation in Continuous Casting by a New In Situ Bending Test Open
The surface quality in continuous casting of the semi-finished product is one of the most important criteria for the successful processing into a finished product. Any defects that may occur should be completely avoided and therefore param…
View article: Scaling Behavior and Surface Quality of High-Strength Low-Alloy Steels with Higher Levels on Cu, Sn, and Ni Under Slab Reheating Conditions
Scaling Behavior and Surface Quality of High-Strength Low-Alloy Steels with Higher Levels on Cu, Sn, and Ni Under Slab Reheating Conditions Open
Nowadays the production of steel from scrap in electric arc furnaces is the most common bridging technology to reduce CO 2 emissions. Depending on scrap quality, a non-negligible content of tramp elements such as Cu, Sn, or Ni is introduce…
View article: On the Role of Tramp Elements for Surface Defect Formation in Continuous Casting of Steel
On the Role of Tramp Elements for Surface Defect Formation in Continuous Casting of Steel Open
In the course of the decarbonization of steel production, electric steel production will continue to gain importance. The processing of low‐quality scrap will also play an important role, which may lead to an increase in the content of so‐…
View article: Influence of Silicon and Tramp Elements on the High-temperature Oxidation of Steel in Direct Casting and Rolling Processes
Influence of Silicon and Tramp Elements on the High-temperature Oxidation of Steel in Direct Casting and Rolling Processes Open
Oxidation processes are unavoidable in continuous casting and further hot processing of steel. A deeper understanding of the occurring phenomena such as intergranular oxidation and liquid metal infiltration of grain boundaries is essential…
View article: The influence of intergranular oxidation on surface crack formation in continuous casting of steel
The influence of intergranular oxidation on surface crack formation in continuous casting of steel Open
High-temperature oxidation phenomena play an important role in steel processing. What is mostly underrated is the importance of internal oxidation in casting processes, namely the continuous casting process. To investigate the impact of in…
View article: High-Temperature Oxidation of Steel under Linear Flow Rates of Air and Water Vapor—An Experimental Determined Set of Data
High-Temperature Oxidation of Steel under Linear Flow Rates of Air and Water Vapor—An Experimental Determined Set of Data Open
High-temperature oxidation phenomena play a crucial role in steel production and processing. The development of new alloying concepts, the modification of production routes due to the decarbonization of steelmaking, and increasing quality …