View article: Polarized Optical Microscopy of Cellulose/Poly(vinyl alcohol) Blend Gel Fibers.
Polarized Optical Microscopy of Cellulose/Poly(vinyl alcohol) Blend Gel Fibers. Open
Cellulose/poly (vinyl alcohol) (PVA) blend gel fibers were prepared by extrusion of the blend solutions in N, N-dimethylacetamide-LiCl from tubular flow field into methanol. Influences of PVA content and flow on the macroscopic orientation…
View article: Crystallization of Poly(p-oxycinnamyl) during Solution Polymerization.
Crystallization of Poly(p-oxycinnamyl) during Solution Polymerization. Open
Poly(p-oxycinnamyl) (POC) crystals were obtained by polyesterification of 4-acetoxy cinnamic acid under elimination of acetic acid in aromatic solvent, Therm-S900. Morphology and structure of the crystals were studied by scanning electron …
View article: Studies on morphology control of polymer crystals during polymerization. 1 Preparation of poly(p-oxybenzoyl) whiskers.
Studies on morphology control of polymer crystals during polymerization. 1 Preparation of poly(p-oxybenzoyl) whiskers. Open
p-アシロキシ安息香酸を液状パラフィンまたはサームS800 (R) 中で重合させることにより, 針状のポリ (p-オキシベンゾイル) 結晶を得た. 重合は静止状態330℃で360分間行った. 得られた針状結晶の密度は, 1.50~1.51g/cm3で単位格子の大きさから求めた結晶密度1.52g/cm3に非常に近い値を示した. また, X線粉末図形では非晶部に基づくピークは認められなかった. 更に, 他の形態を持つ結晶と比較して高い転移温度及び分解温度を示した.これらの事実か…
View article: Studies on morphology control of polymer crystals during polymerization. II Formation mechanism of poly(p-oxybenzoyl) whiskers.
Studies on morphology control of polymer crystals during polymerization. II Formation mechanism of poly(p-oxybenzoyl) whiskers. Open
前報で得たPOB針状結晶が電子線回折図などから高結晶性の延伸鎖型結晶であることを明らかにした. そして, このウイスカの生成機構は, 重合初期生成物の形態観察から次のようなものであると考えた. 溶媒中での縮合によりある重合度に達したオリゴマー分子がラメラ晶として析出する. さらにオリゴマー分子がラメラ晶上に発生したらせん転位に基づいてスパイラル成長で結晶化し, ラメラが高度に積層する. 引き続いて後重合が起こり, ラメラ関のオリゴマー分子が縮合し延伸鎖型結晶となる. また,…