View article: Stress Corrosion Cracking of Manganese Bronze in Water
Stress Corrosion Cracking of Manganese Bronze in Water Open
Continuous and centrifugal cast manganese bronze parts (C86300) experienced intergranular cracking in as few as 24 h after being stored outside. C-ring tests according to ASTM G38 were conducted to assess the material’s susceptibility to s…
View article: Effects of aging and nitridation on microstructure and mechanical properties of austenitic stainless steel
Effects of aging and nitridation on microstructure and mechanical properties of austenitic stainless steel Open
Understanding the effects of in-service microstructural changes in metal alloys on the mechanical performance and remaining life of equipment is a critical part of integrity management in industrial plants. However, the effects of processe…
View article: Strain-ageing effects on the residual low-cycle fatigue life of low-carbon steel reinforcement
Strain-ageing effects on the residual low-cycle fatigue life of low-carbon steel reinforcement Open
Low-cycle fatigue (LCF) failures can be expected when rebars are subjected to a small number of cycles at large stress/strain amplitudes. Major seismic events are often preceded or followed by other events of smaller/larger magnitude. Duri…
View article: Low-cycle fatigue testing on strain-aged steel reinforcing bars
Low-cycle fatigue testing on strain-aged steel reinforcing bars Open
During earthquakes, steel reinforcing bars in reinforced concrete structures may be subjected to large
\ninelastic deformation in tension and compression as high as 6% strain, eventually leading to low-cycle fatigue
\nfailure (Mander, Pant…
View article: Monotonic and low-cycle fatigue properties of earthquake-damaged New Zealand steel reinforcing bars. The experience after the Christchurch 2010/2011 earthquakes
Monotonic and low-cycle fatigue properties of earthquake-damaged New Zealand steel reinforcing bars. The experience after the Christchurch 2010/2011 earthquakes Open
The 2010 and 2011 Christchurch seismic events have highlighted the limitations of the current knowledge in assessing the residual capacity of earthquake-damaged reinforced concrete (RC) buildings. An important challenge during the assessme…
View article: Microstructural Characterization and Image Analysis in Ex-Service Ethylene Pyrolysis Tubes
Microstructural Characterization and Image Analysis in Ex-Service Ethylene Pyrolysis Tubes Open
An abstract is not available for this content so a preview has been provided. As you have access to this content, a full PDF is available via the ‘Save PDF’ action button.