View article: Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking
Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking Open
The article Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I-effect of heat control on welding stresses and stress relief cracking, written by A.
View article: Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment
Correction to: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment Open
The article Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment, written by A. Kromm, T.
View article: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part III: assessment of residual stresses from small-scale to real component welds
Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part III: assessment of residual stresses from small-scale to real component welds Open
For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is …
View article: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking
Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: part I—effect of heat control on welding stresses and stress relief cracking Open
The avoidance of failures during the fabrication or operation of petrochemical reactors made of creep-resistant, low-alloy steels as 13CrMoV9-10 requires still research despite over 60 years of international investigations in the field of …
View article: Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment
Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel Part II: mechanisms of stress relief cracking during post weld heat treatment Open
Welding of 13CrMoV9-10 vanadium steel requires care due to an increased susceptibility to stress relief cracking during post weld heat treatment. Previous research into the crack formation in creep-resistant steels has focused on thermal a…